Nanocrystalline toroidal core provider in China? Transmart Industrial’s nanocrystalline core series include multiple types , For example, nanocrystalline cut cores,nanocrystalline toroidal cores,nanocrystalline tape wound cores,nanocrystalline powder cores, etc.Good materials, advanced production technology, and fine manufacturing techniques are used in the production of nanocrystalline core. Transmart nanocrystalline core suppliers & manufacturers designs transformer core material with to keep it outstanding among similar products. Read additional info at nanocrystalline cores. Transmart Industrial insists on the use of high-quality materials and advanced technology to manufacture soft magnetic materials. Besides, we strictly monitor and control the quality and cost in each production process. All this guarantees the product to have high quality and favorable price.Transmart supplier has a complete and mature service team to provide excellent services for customers and seek mutual benefit with them.
As the iron core of the transformer, generally 0.35mm thick cold-rolled silicon steel sheet is selected. It is cut into long pieces according to the size of the required iron core, and then overlapped into “day” shape or “mouth” shape. In principle, in order to reduce eddy current, the thinner the silicon steel sheet, the narrower the spliced strip, and the better the effect. This not only reduces the eddy current loss and temperature rise, but also saves the material of silicon steel sheet. But in fact, when making silicon steel sheet iron core. Not only from the above favorable factors, because making the iron core in that way will greatly increase the working hours and reduce the effective section of the iron core. Therefore, when making transformer iron core with silicon steel sheet, we should start from the specific situation, weigh the advantages and disadvantages and choose the best size.
Hysteresis loss is the iron loss caused by the hysteresis phenomenon in the magnetization process of the iron core. The size of this loss is directly proportional to the area surrounded by the hysteresis loop of the material. The hysteresis loop of silicon steel is narrow, and the hysteresis loss of transformer core made of silicon steel is small, which can greatly reduce its heating degree. Since silicon steel has the above advantages, why not use the whole silicon steel as the iron core and process it into a sheet? rolled silicon steel sheet is selected. It is cut into long pieces according to the size of the required iron core, and then overlapped into “day” shape or “mouth” shape. In principle, in order to reduce eddy current, the thinner the silicon steel sheet, the narrower the spliced strip, and the better the effect. This not only reduces the eddy current loss and temperature rise, but also saves the material of silicon steel sheet. But in fact, when making silicon steel sheet iron core. Not only from the above favorable factors, because making the iron core in that way will greatly increase the working hours and reduce the effective section of the iron core. Therefore, when making transformer iron core with silicon steel sheet, we should start from the specific situation, weigh the advantages and disadvantages and choose the best size.
As one of Transmart Industrial’s multiple product series, mumetal cores series enjoy a relatively high recognition in the market. Transmart Industrial provides diversified choices for customers. The mu-metal cores are available in a wide range of types and styles, in good quality and in reasonable price.Transmart Industrial effectively improves after-sales service by carrying out strict management. This ensures that every customer can enjoy the right to be served. Find more information on https://www.transmart.net/.
Amorphous nanocrystalline alloys are competing with soft ferrite in the field of medium and high frequency. In 10kHz to 50KHz electronic transformer, the working magnetic flux density of iron-based nanocrystalline alloy can reach 0.5T and the loss P0.05 5 / 20K ≤ 25W / kg, so it has obvious advantages in high-power electronic transformer. In 50 kHz to 100 kHz electronic transformer, the loss of iron-based nanocrystalline alloy is P0.05 2 / 100k is 30 ~ 75W / kg, Fe based amorphous alloy P0.05 2 / 100k is 30W / kg, which can replace some ferrite markets.
Characteristics and application of nanocrystalline magnetic core: High permeability, nanocrystalline Fe73 5Cu1Nb3Si13. 5B9 alloy has high saturation magnetic induction. The material becomes brittle after heat treatment and is easy to be processed into alloy powder. Compared with the nanocrystalline magnetic core wound with strip, the magnetic permeability of the nanocrystalline magnetic core is still very low and the soft magnetic properties are unstable. At present, the urgent problems to be solved are as follows: 1. Effectively control the growth of nanocrystals during heat treatment; 2. Molding of magnetic particle core; 3 Effect of heat treatment specification on soft magnetic properties of magnetic particle core.